High surface area carbonous components from emulsion derived SiOC and their gas sensing behavior

  Articoli su Riviste JCR/ISI  (anno 2015)

Autori:  Vakifahmetoglu C., Buldu M., Karakuscu A., Ponzoni A., Assefa D., Soraru G

Affiliazione Autori:  - Department of Mechanical Engineering, Istanbul Kemerburgaz University, 34217 Istanbul, Turkey - SENSOR Lab, CNR-INO and Department of Information Engineering, University of Brescia, Brescia, Italy - Dipartimento di Ingegneria Industriale, Università di Trento, Via Sommarive 9 38123 Trento, Italy

Riassunto:  A commercially available liquid polysiloxane polymer was emulsified via stirring in the presence of water and surfactant. After curing, porous microbead/capsule thermosets were obtained. The samples kept their shape upon pyrolysis and resulted in SiOC ceramics which were etched by hydrofluoric acid at room temperature. The specific surface area of the components increased considerably reaching to 310 m(2)/g when etching process was conducted. It was shown that the samples had hierarchical porosity including micro-meso and macro porosity (5-10 micron range). The etching process affected the conductivity and the room temperature NO2 sensing capability of the SiOC samples. It is shown that porous SiOC and carboneous materials produced via hydrofluoric acid etching, can be used to detect NO2 (5 ppm) at room temperature (for the etched sample) with an easy-to-read conductance (mS range) as well as fast response kinetics (few minutes) and a complete signal recovery. (C) 2015 Elsevier Ltd. All rights reserved.

Rivista/Giornale:  Journal of the European Ceramic Society
Volume n.:  35 (16)      Pagine da: 4447  a: 4452
Ulteriori informazioni:  C.V. and M.B. gratefully acknowledge the support of TUBITAK (The Scientific and Technological Research Council of Turkey) under the project Grant No: CAYDAG-113Y533.
DOI: 10.1016/j.jeurceramsoc.2015.08.030

*Impact Factor della Rivista: (2015) 2.933   *Citazioni: 13
data tratti da "WEB OF SCIENCE" (marchio registrato di Thomson Reuters) ed aggiornati a:  14/07/2019

Riferimenti visionabili in IsiWeb of Knowledge: (solo per sottoscrittori)
Per visualizzare la scheda dell'articolo su IsiWeb: Clicca qui
Per visualizzare la scheda delle Citazioni dell'articolo su IsiWeb: Clicca qui

INO © Istituto Nazionale di Ottica - Largo Fermi 6, 50125 Firenze | Tel. 05523081 Fax 0552337755 - P.IVA 02118311006     P.E.C.    Info